Abstract

A high-carbon steel wire rod of high ductility for steel cord and the like is provided that experiences little breakage during drawing. The high-carbon steel wire rod of high ductility is a high-carbon steel wire rod fabricated by hot rolling that that has a carbon content of 0.7 mass % or greater, wherein 95% or greater of the wire rod metallographic structure is pearlite structure and the maximum pearlite block size of pearlite at the core of the hot-rolled wire rod is 65 μm or less. The high-carbon steel wire rod of high ductility has a tensile strength in a range of {248+980×(C mass %)}±40 MPa} and a reduction of area of {72.8−40×(C mass %) %} or greater. The high-carbon steel wire rod of high ductility is characterized in that the average pearlite block size at the core of the hot-rolled wire rod constituted by ferrite grain boundaries of an orientation difference of 9 degrees or greater as measured with an EBSP analyzer is 10 μm or greater and 30 μm or less.