Abstract

A Cu-based sintered sliding member that can be used under high-load conditions. The sliding member is age-hardened, including 5 to 30 mass % Ni, 5 to 20 mass % Sn, 0.1 to 1.2 mass % P, and the rest including Cu and unavoidable impurities. In the sliding member, an alloy phase containing higher concentrations of Ni, P and Sn than their average concentrations in the whole part of the sliding member, is allowed to be present in a grain boundary of a metallic texture, thereby achieving excellent wear resistance. Hence, without needing expensive hard particles, there can be obtained, at low cost, a Cu-based sintered sliding member usable under high-load conditions. Even more excellent wear resistance is achieved by containing 0.3 to 10 mass % of at least one solid lubricant selected from among graphite, graphite fluoride, molybdenum disulfide, tungsten disulfide, boron nitride, calcium fluoride, talc and magnesium silicate mineral powders.