A method of manufacturing an austenitic stainless steel, being dissolved and refined, by providing Si from 0.2 to 2.0% by mass, Mn from 0.3 to 5.0% by mass, S at 0.007% by mass or less, Ni from 7.0 to 15.0% by mass, Cr from 15.0 to 20.0% by mass, Al at 0.005% by mass or less, Ca at 0.002% by mass or less, Mg at 0.001% by mass or less, and 0 from 0.002 to 0.0065% by mass and setting a ratio, during refining, of CaO/SiO₂ in a slag between 1.0 and 2.5. The remainder comprises Fe and unavoidable impurities, and a mass ratio indicated by (Mn+Si)/Al among Mn, Si, and Al is 200 or more. An oxide-based nonmetallic inclusion comprises MnO—SiO₂—Al₂O₃—CaO, where Al₂O₃ is 30% by mass or less, Cr₂O₃ is 5% by mass or less, and MgO is 10% by mass or less, and a sulfide-based nonmetallic inclusion is CaS whose maximum area is 100 μm² or less.