Abstract

This hot work tool steel has a composition containing C: 0.45 to 0.57 mass %, Si: 0.05 to 0.30 mass %, Mn: 0.45 to 1.00 mass %, Cr: 4.5 to 5.2 mass %, Ni: 0.5 mass % or less, Mo+(½) W: 1.0 to 2.0 mass %, V: 0.30 to 0.80 mass %, and N: 0.008 to 0.025 mass %, the remainder being Fe and unavoidable impurities, and the area ratio of carbide having an equivalent circle diameter of 1 μm or less being 20% or higher. It is thereby possible to improve thermal conductivity to thereby shorten cycle time, and improving hardness after heat treatment to improve abrasion resistance while sufficient hardenability is maintained. Consequently, it is possible to obtain a hot work tool steel having excellent toughness with high hardness, excellent corrosion resistance, and minimal degradation of machinability.