Abstract

A La-element micro-alloyed AlCrFeNiTi bulk alloy with high corrosion resistance and wear resistance and a preparation method therefor and applications thereof are provided. The alloy includes the following chemical components in corresponding percentages: 2.05 wt % to 2.15 wt % of Al, 20.50 wt % to 20.65 wt % of Cr, 34.50 wt % to 35.54 wt % of Ni, 18.80 wt % to 19.16 wt % of Ti, 1.05 wt % to 1.15 wt % of La, and the balance of Fe and inevitable impurities, wherein the chemical components need to meet the following three relations at the same time: (1) 18.57≤Fe/La≤22.00; (2) 6.47≤Fe/(La+Al)≤7.45; and (3) 1.05≤Fe/(La+Ti)≤1.16. Compared with AISI 310S stainless steel, the alloy is improved by 280% to 290% in hardness, reduced by 4% to 7% in friction coefficient, and reduced by 17% to 34% in wear amount, increased by 73% to 77% in self-corrosion potential, and decreased by 96% in corrosion current density on average.