Abstract

The abrasion resistance of siliceous filler-reinforced rubber vulcanizates is improved by adding to the unvulcanized rubber composition a silane coupling composition comprising a mixture of a silane coupling agent, such as (a) organic silane compounds containing an internal active olefinic linkage, (b) bis(alkoxysilylalkyl)polysulfides, (c) haloalkylsilanes, and (d) silane compounds containing a vinyl functional group in the organofunctional portion of the compound, and an alkyl alkoxysilane, such as methyltrimethoxysilane. The silane coupling agent is present in coupling amounts, e.g., between 0.1 and 50 parts per hundred parts of rubber, and the weight ratio of mercaptosilane to alkyl alkoxysilane is between 0.15:1 and 15:1. Preferably, the silanes are in a ratio of about 1:1, are admixed with a hydrocarbon process oil and the oil-silane mixture added to the siliceous filler-rubber mixture.