Abstract

A burnable-absorber-containing zirconium alloy is described for application to the inside surface of cladding tubes for light water nuclear reactors. The alloy comprises naturally occurring erbium in a range from a measurable amount up to about 20 wt. % or isotopically purified erbium-167 in a range from a measurable amount up to about 5 wt. %; tin in a range from a measurable amount up to about 0.5 wt. %; iron in a range from a measurable amount up to about 0.2 wt. %; chromium in a range from a measurable amount up to about 0.1 wt. %; niobium in a range from a measurable amount up to about 0.1 wt. %; silicon in a range from about 50 to about 120 parts per million ('ppm'); oxygen in a range from a measurable amount up to about 800 ppm; and the balance zirconium. Such an alloy provides an effective absorber material for reactor control, while providing adequate mechanical properties and corrosion resistance for the intended application.