Abstract

A low temperature sealing composition consists essentially of 45.0 to 85.0 wt. % of PbO, 1.0 to 11.0 wt. % of B.sub.2 O.sub.3, 1.0 to 45.0 wt. % of Bi.sub.2 O.sub.3, 0.2 to 10.0 wt. % of Fe.sub.2 O.sub.3, 0 to 15.0 wt. % of ZnO, 0 to 5.0 wt. % of CuO, 0 to 5.0 wt. % of V.sub.2 O.sub.5, 0 to 3.0 wt. % of SnO.sub.2, 0 to 5.0 wt. % of SiO.sub.2 plus Al.sub.2 O.sub.3, 0 to 7.0 wt. % of BaO, 0 to 5.0 wt. % of TiO.sub.2, 0 to 5.0 wt. % of ZrO.sub.2 and 0 to 6.0 wt. % of F.sub.2. The sealing composition has a low sealing temperature of 400.degree.C. or lower and is useful for readily sealing IC packages and display panels without application of load. In order to adjust the thermal coefficient of expansion, the sealing glass composition may be used by mixing with 20 vol. % to 55 vol. % of refractory filler powder of such as lead titanate based ceramics, willemite based ceramics, cordierite ceramics, zircon based ceramics or tin oxide based ceramics.